CLOVAMASTIC - PART A (1:1)

Use
Suitable for use as a one or two coat primer/finish coating or as an intermediate coating over recommended anti-corrosive primers. Ideal for
immersion or non-immersion service for storage tanks, oil and gas equipment, structural steel, pulp and paper mills, sewage treatment
plants, water treatment plants, marine and other heavy industrial areas. Ideal as a one-coat maintenance finish coat over Zinc Rich primers

Surfaces preparation 
Surface to be coated must be clean, dry and free from loose mill scale, weld spatter, oil, grease or other contaminants. Minimum surface
preparation for steel in non-immersion service is SSPC-SP2. For immersion service an SSPC SP10 "Near White Blast" is required. Existing
finishes should be tested for film integrity. If found to be sound, apply several test patches and inspect adhesion, lifting or wrinkling before
proceeding with the project. A minimum SSPC-SP6 is recommended when using 83110BX Summer Grade Activator.

Recommended primer
STEELSelf Priming or 83 Series Zinc Rich Primers
CONCRETESelf Priming
GALVANIZEDSelf Priming
ALUMINUMSelf Priming * An SSPC SP-16 Brush-Off Blast is recommended

Required tools 
Airless Spray: Minimum tip pressure: 5100psi. Minimum pump size: 56:1@100psi air line. Tip sizes .021" - .025"
Brush/Roller: Can be brushed or rolled but lap marks will be visible.

How to use
Mixing
Mix base A component and Activator 83110 B or BX separately with good agitation. Add Activator to base A component and mix
thoroughly until homogenous. Allow to react in can for 15 minutes (induction time). If thinning is necessary or required (up to 10%),
proceed only after recommended induction time has passed. For application during hotter weather when longer open times are
required, summer grade activator 83110BX can be used.

Thinner 
C-25 Fast Evaporating

Film thickness
Wet: 8 - 12 mils
Dry: 6 -10 mils

Drying time



Limitation
Do not use for potable water service. This epoxy product will chalk and yellow with age however this will not affect performance of
the coating. Application should not proceed when the relative humidity is above 85%. Not recommended for overcoating loose rust,
mill scale, salts or other contaminants which may be on the surface. * Use of 83110B Regular and 83110BX Summer Grade
Activators will result in slightly different colour / appearance of the cured coating. Do not mix B and BX Activators on the same job.