CLOVATAR 22 - COL TAR EPOXY PART B - 3,78L
Product Code: 83022B01
Description :
ClovaTar 22 is a high build, (16 to 18 mils per coat) abrasion and chemical resistant coating that provides outstanding protection for steel or concrete in harsh environments. The high build capability allows for one coat application and substantially lower applied labor costs. Suitable for sustained immersion in fresh or salt water and certain other industrial chemicals. Not suitable for potable water service. ClovaTar 22 is a two component product with base 83022 A and converter 83022 B supplied in separate containers. A rust inhibitive primer is recommended for steel surfaces where superior corrosion resistance is required. ClovaTar 22 meets the performance requirements on and is approved under MPI #35 Bituminous Coatings.
Recommended use :
Typical areas of use are ship hulls, pilings, below grade tanks, waste treatment facilities, process equipment, clarifiers and other areas where maximum resistance to corrosion and abrasion are required.
ClovaTar 22 is a high build, (16 to 18 mils per coat) abrasion and chemical resistant coating that provides outstanding protection for steel or concrete in harsh environments. The high build capability allows for one coat application and substantially lower applied labor costs. Suitable for sustained immersion in fresh or salt water and certain other industrial chemicals. Not suitable for potable water service. ClovaTar 22 is a two component product with base 83022 A and converter 83022 B supplied in separate containers. A rust inhibitive primer is recommended for steel surfaces where superior corrosion resistance is required. ClovaTar 22 meets the performance requirements on and is approved under MPI #35 Bituminous Coatings.
Recommended use :
Typical areas of use are ship hulls, pilings, below grade tanks, waste treatment facilities, process equipment, clarifiers and other areas where maximum resistance to corrosion and abrasion are required.
Use
Typical areas of use are ship hulls, pilings, below grade tanks, waste treatment facilities, process equipment, clarifiers and
other areas where maximum resistance to corrosion and abrasion are required.
Surface preparation
Surface to be coated must be clean, dry and free from loose mill scale, weld spatter and other contamination. For
maximum performance, perparation to an SSPC-SP6 Commercial Blast Cleaning is recommended. For immersion
service, prepare to an SSPC-SP10 Near White Blast Cleaning. Blast surfaces must be coated before flash rusting is
allowed to occur. Concrete must be dry and aged a minimum of 28 days. Acid etch or sweep blast to provide a profile
on smooth concrete or non-ferrous metals.
Recommended primer
STEEL Self Priming/ ClovaPrime 21/ 83001 ClovaZinc 1/ 83002 ClovaZinc 2
CONCRETESelf--priming (see Surface Prep)
GALVANISEDSelf--priming (see Surface Prep)
ALUMINUMSelf--priming (see Surface Prep)
Required tools
AIRLESS SPRAY Speeflo Commander 45:1 with tip sizes .021" - .023" or equivalent
H.V.L.P. Binks Model Mach 1 905 x 905AP (pressure) or equivalent
CONVENTIONAL Binks Model 95GUN 63SS X 63PB (pressure) or equivalent
BRUSH / ROLLER Brushing is limited to small areas or touch-up
How to use
Mixing
Mix base A and curing agent B separately with good agitation. Add converter B or curing agent to base component
and mix thoroughly until homogenous. Allow to react in can for 15 minutes (induction time). If thinning is necessary or
required, proceed only after recommended induction time has passed. In cool weather, product will perform better if
kept at room temperature: 21o - 26oC (70o - 80oF).
Thinner
C-70 Slow Evaporating
C-25 Fast Evaporating
Film Thickness
Wet: 21 - 24 mils
Dry: 16 - 18 mils
Drying time
Limitation
Not suitable for potable water. For best results apply when substrate temperature is above 10oC (50oF), and at a
minimum of 3oC (5oF) above the dew point. Do not apply when relative humidity is above 85%. Immersion service in
salt or fresh water requires a pinhole free dry film thickness of 16 to 18 mils. Coating must be fully cured before being
placed into immersion service. Do not exceed maximum overcoat intervals. Consult with your Cloverdale Paint
Representative on the overcoat interval that matches your application conditions as maximum overcoat intervals are
reduced with increased temperatures.
Typical areas of use are ship hulls, pilings, below grade tanks, waste treatment facilities, process equipment, clarifiers and
other areas where maximum resistance to corrosion and abrasion are required.
Surface preparation
Surface to be coated must be clean, dry and free from loose mill scale, weld spatter and other contamination. For
maximum performance, perparation to an SSPC-SP6 Commercial Blast Cleaning is recommended. For immersion
service, prepare to an SSPC-SP10 Near White Blast Cleaning. Blast surfaces must be coated before flash rusting is
allowed to occur. Concrete must be dry and aged a minimum of 28 days. Acid etch or sweep blast to provide a profile
on smooth concrete or non-ferrous metals.
Recommended primer
STEEL Self Priming/ ClovaPrime 21/ 83001 ClovaZinc 1/ 83002 ClovaZinc 2
CONCRETESelf--priming (see Surface Prep)
GALVANISEDSelf--priming (see Surface Prep)
ALUMINUMSelf--priming (see Surface Prep)
Required tools
AIRLESS SPRAY Speeflo Commander 45:1 with tip sizes .021" - .023" or equivalent
H.V.L.P. Binks Model Mach 1 905 x 905AP (pressure) or equivalent
CONVENTIONAL Binks Model 95GUN 63SS X 63PB (pressure) or equivalent
BRUSH / ROLLER Brushing is limited to small areas or touch-up
How to use
Mixing
Mix base A and curing agent B separately with good agitation. Add converter B or curing agent to base component
and mix thoroughly until homogenous. Allow to react in can for 15 minutes (induction time). If thinning is necessary or
required, proceed only after recommended induction time has passed. In cool weather, product will perform better if
kept at room temperature: 21o - 26oC (70o - 80oF).
Thinner
C-70 Slow Evaporating
C-25 Fast Evaporating
Film Thickness
Wet: 21 - 24 mils
Dry: 16 - 18 mils
Drying time
Limitation
Not suitable for potable water. For best results apply when substrate temperature is above 10oC (50oF), and at a
minimum of 3oC (5oF) above the dew point. Do not apply when relative humidity is above 85%. Immersion service in
salt or fresh water requires a pinhole free dry film thickness of 16 to 18 mils. Coating must be fully cured before being
placed into immersion service. Do not exceed maximum overcoat intervals. Consult with your Cloverdale Paint
Representative on the overcoat interval that matches your application conditions as maximum overcoat intervals are
reduced with increased temperatures.
Available color
Black
Black
Available formats
3.78 L (3.02L Part A + 0.76L Part B)
18.9L (15.12L Part A + 3.78L Part B)
3.78 L (3.02L Part A + 0.76L Part B)
18.9L (15.12L Part A + 3.78L Part B)