DTM POLYURETHANE ENAMEL 835 - CLEAR BASE - PART A (9:1) 17,10L (14,66L + COLORATION)
Product Code: 83503A05
Description :
A cost-effective, two-component modified aliphatic polyurethane coating available in either very high gloss or low
sheen finishes designed for use where superior performance is required but cannot be achieved using conventional
coatings. DTM Polyurethane can be applied directly to properly prepared steel and has been formulated with low odor
solvents, making it ideal for shop use.
Recommended uses :
This product was designed to provide durability in an industrial environment. For use on industrial machinery and
equipment, oil and gas process equipment, pipe racks, storage tank exteriors, drilling and service equipment and
structural steel. Not recommended for immersion service or high corrosion areas.
A cost-effective, two-component modified aliphatic polyurethane coating available in either very high gloss or low
sheen finishes designed for use where superior performance is required but cannot be achieved using conventional
coatings. DTM Polyurethane can be applied directly to properly prepared steel and has been formulated with low odor
solvents, making it ideal for shop use.
Recommended uses :
This product was designed to provide durability in an industrial environment. For use on industrial machinery and
equipment, oil and gas process equipment, pipe racks, storage tank exteriors, drilling and service equipment and
structural steel. Not recommended for immersion service or high corrosion areas.
This Kit Contains:
- DTM POLYURETHANE ENAMEL 835 - PART B (9:1)* (x 1)
Use
This product was designed to provide durability in an industrial environment. For use on industrial machinery and
equipment, oil and gas process equipment, pipe racks, storage tank exteriors, drilling and service equipment and
structural steel. Not recommended for immersion service or high corrosion areas.
Surfaces preparation
Surfaces to be coated must be clean, dry and free of oil, grease or other contaminants. All mill scale and weld spatter
must be removed for maximum peformance. A minimum SSPC-SP3 Power Tool Cleaning is recommended but an
SSPC-SP6 Commercial Blast Cleaning will provide improved product performance. Non ferrous metals must be
washed and etched with 78100 Clova Clean prior to priming and topcoating.
Recommended primer
STEEL Self Priming
CONCRETENot Recommended
GALVANIZED83021 Clova Prime 21 or equivalent epoxy primer
ALUMINUM83021 Clova Prime 21 or equivalent epoxy primer
Recommended tools
AIRLESS SPRAY Speeflo Atlas 30:1 with tip sizes .013" - .015" or equivalent
H.V.L.P. Binks Model Mach 1 94 x 97AP (pressure) or equivalent
CONVENTIONAL Binks Model 95GUN 63CSS X 63PB (pressure) or equivalent
BRUSH / ROLLER Brushing and rolling is limited to small areas or for touch up.
How to use
Mixing
Mix nine parts 835 Series A with one part 83500 B until homogenous. Allow to react in can for 15 minutes (induction
time). If thinning is necessary or required, proceed only after induction time has passed.
Thinner
78011 Xylene
Film thickness
Wet: 2.75 - 7.5 mils
Dry: 1.25 - 3.5 mils
Drying time
Temperature, Relative Humidity, and Film Thickness will affect dry and re-coat times.
Limitations
Not for severely corrosive environments. Can protect against mild chemicals and solvent exposures. Not for
immersion service. Proper breathing attire must be worn during application.
This product was designed to provide durability in an industrial environment. For use on industrial machinery and
equipment, oil and gas process equipment, pipe racks, storage tank exteriors, drilling and service equipment and
structural steel. Not recommended for immersion service or high corrosion areas.
Surfaces preparation
Surfaces to be coated must be clean, dry and free of oil, grease or other contaminants. All mill scale and weld spatter
must be removed for maximum peformance. A minimum SSPC-SP3 Power Tool Cleaning is recommended but an
SSPC-SP6 Commercial Blast Cleaning will provide improved product performance. Non ferrous metals must be
washed and etched with 78100 Clova Clean prior to priming and topcoating.
Recommended primer
STEEL Self Priming
CONCRETENot Recommended
GALVANIZED83021 Clova Prime 21 or equivalent epoxy primer
ALUMINUM83021 Clova Prime 21 or equivalent epoxy primer
Recommended tools
AIRLESS SPRAY Speeflo Atlas 30:1 with tip sizes .013" - .015" or equivalent
H.V.L.P. Binks Model Mach 1 94 x 97AP (pressure) or equivalent
CONVENTIONAL Binks Model 95GUN 63CSS X 63PB (pressure) or equivalent
BRUSH / ROLLER Brushing and rolling is limited to small areas or for touch up.
How to use
Mixing
Mix nine parts 835 Series A with one part 83500 B until homogenous. Allow to react in can for 15 minutes (induction
time). If thinning is necessary or required, proceed only after induction time has passed.
Thinner
78011 Xylene
Film thickness
Wet: 2.75 - 7.5 mils
Dry: 1.25 - 3.5 mils
Drying time
Temperature, Relative Humidity, and Film Thickness will affect dry and re-coat times.
Limitations
Not for severely corrosive environments. Can protect against mild chemicals and solvent exposures. Not for
immersion service. Proper breathing attire must be worn during application.
Available colors
White, Black, Factory-Mixed and Custom Colors
White, Black, Factory-Mixed and Custom Colors
Available formats
3.78L (3.40L Part A + 0.38L Part B)
18.9L (17.01L Part A + 1.9L Part B)
3.78L (3.40L Part A + 0.38L Part B)
18.9L (17.01L Part A + 1.9L Part B)